Superhydrophobic-electrochromic PEDOT/PFHP bilayer surfaces


Caglar A., Yildirim M., CENGİZ U., KAYA İ.

THIN SOLID FILMS, cilt.619, ss.187-194, 2016 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 619
  • Basım Tarihi: 2016
  • Doi Numarası: 10.1016/j.tsf.2016.10.070
  • Dergi Adı: THIN SOLID FILMS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.187-194
  • Anahtar Kelimeler: Electrochromism, Superhydrophobic surfaces, Multilayer surfaces
  • Çanakkale Onsekiz Mart Üniversitesi Adresli: Evet

Özet

Firstly, highly soluble perfluorohexyl substituted pyrrole polymer (PFHP) was synthesized by one-step reaction and characterized using spectral characterization techniques. Monolayer PFHP films were deposited on ITO-glass plates by dip and spin-coating techniques using the THF and DCM solutions. Bilayer PEDOT/PFHP films were prepared in two steps: 1) Electrochemical deposition of PEDOT layer on ITO-glass surface, 2) PFHP top layer coating on PEDOT layer by dip and spin-coating techniques. Experimental conditions in coatings were varied to optimize the surface properties like hydrophobicity. SEM-EDX analyses were carried out to determine the surface characteristics. Water and oil contact angles (WCA and OCA) were measured by Attention Theta contact angle meter. Deposition of PFHP solutions on ITO-glasses formed relatively flat surfaces having low WCA and OCA. Bilayer PEDOT/PFHP had highly porous surfaces and increased WCA values up to >170 degrees. The films prepared from DCM solutions had higher WCA values due to the formation of surface morphology. Electrochromic properties of superhydrophobic bilayer PEDOT/PFHPwere also examined by spectroelectrochemical analysis. 20-25% of transmittance changes were obtained at two different absorption bands between the neutral and doped states. (C) 2016 Elsevier B.V. All rights reserved.