In this study, Nanofiber Polyvinylidene fluoride (PVDF) membranes was produced by electon spinning method and examined by absorbition performances. To improve membranes’ seperation performances, natural zeolite (clinoptilolite) was used in 0, 2, 4% rates. In membrane seperation progress, membranes’ material absorbition mechanism was set on with experimental optimization. In experimental optimization dyed matter concentration (5-10-15 mg/L), natural zeolite (clinoptilolite) rate (0-2-4%) and absorbation dosage (0.01-0.015-0.02 g) effect was examined. Optimized conditions was set as 10 mg/L dye concentration, 0,02 g amount of absorbition and 2% as contribution rate. It is approved that these isoterm tests were compatible with Langmiur isoterm. Therefore, active points in PVDF absorbition surface were homogenous and single layered absorbition was occured.
Bu çalışmada, elektro eğirme tekniği ile nanofiber poliviniliden florür (PVDF) membranlar üretilmiş ve membranların adsorpsiyon performansları incelenmiştir. Membranların ayırma performanslarını iyileştirmek için içerisine doğal zeolit (klinoptilolit) %0, 2, 4 oranında eklenmiştir. Membran ayırımı sırasında, membranın malzemeyi adsorplama mekanizması deneysel optimizasyon ile belirlenmiştir. Deneysel optimizasyonda boyar madde konsantrasyonu (5-10-15 mg/L), doğal zeolit (klinoptilolit) oranı (%0-2-4) ve adsorbent dozajının (0.01-0.015-0.02 g) etkisi incelenmiştir. Optimum koşullar olarak 10 mg/L boya konsantrasyonu, 0,02 g adsorbent miktarı ve %2 katkı oranı olarak belirlenmiştir. Yapılan izoterm çalışmaları Langmuir izotermine uyum göstermiştir. Dolayısıyla PVDF adsorbent yüzeyindeki aktif noktalar homojen dağılımlıdır ve tek katmanlı adsorpsiyon gerçekleşmiştir.